Ammonia Stress Corrosion Cracking||API571||Damage mechanism скачать в хорошем качестве

Ammonia Stress Corrosion Cracking||API571||Damage mechanism

Ammonia Stress Corrosion Cracking Description of Damage a) Aqueous streams containing ammonia may cause SCC in some copper alloys. b) Carbon steel is susceptible to SCC in anhydrous ammonia. Affected Materials a) Copper-zinc alloys (brasses, especially as zinc increases above 15 %), including admiralty brass and aluminum brasses, in environments with aqueous ammonia and/or ammonium compounds. b) Carbon steel, especially high-strength steel, in anhydrous ammonia. Amine stress corrosion cracking    • Amine Stress Corrosion Cracking||API571||D...   475°C embrittlement    • 885 °F (475 °C) Embrittlement|| API 571 | ...